high-quality PVB interlayer for laminated glass in architecture and automotive. Awarded the ISO 9001:2015 and IATF16949.

PVB Film Test Report
Sample:0.76mm Clear PVB Film
ITEM	STANDARD
Thickness(mm)	±0.02mm
Light Transmittance(%)	≥81%
Haze(%)	≤0.6
Moisture(%)	0.3%-0.55%
Thermal Shrinkage (80℃/15min)	≤15
Surface Roughness(RZ)	15-55(RZ)
Tensile Strength(Mpa)	≥20Mpa(200kg/300mm)
Elongation(%)	≥200%
High Temperature Impact	Sample after 4 hours in 40℃, 225g steel ball fall from 10m height, not go through the sample.
Low Temperature Impact	Samle after 4 hours in -20℃, 225g steel ball fall from 8m height,not go through the sample,test not alow pause.
UV Test	No obvious change after 100 hours UV Light in 45℃±5℃ test chamber, transmittance decrease≤10%
Continous Knock	3-7 level
Penetration resistance	2260g±10g steel ball fall from 5m,could not broke diameter 75mm hole.
Heat Resistance	alow glass gap in 100℃ water after 2 hours.but that will affect usage the bulbs and orhter shortage not allowed.
Falling Ball Impact	1040g±10g steel ball fall from 1200mm height, laminated glass borke not allowed. If the glass broke, the mid PVB interlayer not allowed borke and exposed to the air.
Yellow Index	≤6
Melt Index	1.1g-1.5g/10min